Structural-phase junctions in the system of Pt–Si during rapid thermal treatment
https://doi.org/10.29235/1561-8323-2020-64-2-238-244
Abstract
In recent years the interest to silicides significantly rose relating to their huge potentialities as the material of the low-Ohm contacts and interconnections of metallization of the silicon integrated circuits. In view of this the necessity appeared to consider more extensively the thermal dynamic, electric and structural peculiarities of their formation. Purpose of the work was in investigation of influence of the rapid thermal treatment on the structural –phase junctions in the system of Pt–Si during formation of platinum silicide. As samples, the Pt films were used, 43.7 nm thick and applied on the substrates of the mono-crystal silicon KEF КЭФ 0.5 with orientation (111) by means of the magnetron sputtering of the platinum target with purity of 99.95 % on the unit MRS 603 with the cryogenic pumping to the pressure not worse, than 5 · 10–5 Pa. As the operating medium, argon was used, whose purity constituted 99.933 %. Rapid thermal treatment was performed in the nitrogen medium within the temperature range from 200 to 550 °С with a step of 50 °С and the time period of 7 s. The process of interaction of platinum with silicon during treatment of the Pt–Si system was evaluated by means of the analysis of the RBS spectra. It is demonstrated, that within the temperature range of 200 °С ≤ Т ≤ 300 °С during 7 s of the rapid thermal process on the boundary of the metal film with the substrate, formation takes place of the Pt2Si layer owing to diffusion of the Pt atoms into silicon via the layer of the growing silicide. The temperature Т = 300 °С is peculiar for the complete application of the Pt film during 7 s in process of the silicide formation of the single phase system of Pt2Si. At 350 °С ≤ Т < 450 °С formation is registered of the double phase system of Pt2Si → PtSi, starting from the inter-phase boundary of Si/Pt2Si predominantly owing to the opposite diffusion of the Si atoms into the layer of Pt2Si. The temperature of the rapid thermal treatment Т = 450 °С marks formation of the thermally stable balanced structure of PtSi along the entire silicide thickness, which is 50–100 °С lower and considerably more rapid, than during the long-term balanced thermal treatment.
About the Authors
U. A. Pilipenka
Holding Managing Company “Integral”
Belarus
Belarus
Pilipenka Uladzimir A. – Corresponding Member, D. Sc. (Engineering), Professor, Deputy Director.
121a, Kazinets Str., 220108, Minsk
F. F. Komarov
A. N. Sevchenko Institute of Applied Physical Problems of Belarusian State University
Belarus
Belarus
Komarov Fadey F. – Corresponding Member, D. Sc. (Physics and Mathematics), Professor, Head of the Laboratory.
7, Kurchatov Str., 220045, Minsk
V. A. Saladukha
Holding Managing Company “Integral”
Belarus
Belarus
Saladukha Vitali A. – Ph. D. (Engineering), General Manager.
121a, Kazinets Str., 220108, Minsk
V. A. Harushka
Holding Managing Company “Integral”
Belarus
Belarus
Harushka Valiantsina A. – Leading engineer.
121a, Kazinets Str., 220108, Minsk
References
1. Murarka Sh. P. Silicides for VLSI Applications. Academic Press, 1983. 200 p.
2. Faber E. J., Wolters R. A. M., Schmitz J. On the kinetics of platinum silicide formation. Applied Physics Letters, 2011, vol. 98, no. 8, pp. 082102 (1–3). https://doi.org/10.1063/1.3556563
3. Solodukha V. A., Turtsevich A. S., Solov’ev Y. A., Komarov F. F., Mil’chanin O. V., Kovaleva T. B., Gaponenko S. V. Formation of the nickel-platinum alloy silicide Schottky barriers. Russian Microelectronics, 2014, vol. 43, no. 1, pp. 1–8. https://doi.org/10.1134/s1063739713050077
4. Komarov F. F., Milchanin O. V., Kovalyova T. B., Saladukha V. A., Solovjov J. A., Turtsevich A. S. Low Temperature Formation of the Platinum Silicide Contact Layer for the Schottky Diodes. Doklady Natsional’noi akademii nauk Belarusi = Doklady of the National Academy of Sciences of Belarus, 2013, vol. 57, no. 2, pp. 38–42 (in Russian).
5. Borisenko V. E., Hesketh P. J. Rapid Thermal Processing of Semiconductors. New York, London, 1997. https://doi.org/10.1007/978-1-4899-1804-8
6. Pilipenko V. A., Ponomar V. N., Gorushko V. A. Property Control of the Thin-Film Systems with Application of the Pulse Photon Treatment. Inzhenerno-Fizicheskii Zhurnal = Journal of Engineering Physics and Thermophysics, 2003, vol. 76, no. 4, pp. 95–98 (in Russian).
7. Ievlev V. M., Soldatenko S. A., Kushev S. B., Gorozhankin Yu. V., Vakhtel V. M. Effect of Photon Activation during the Synthesis of Silicide Films in the Heterosystem (111) Si–Ni–Pt. Kondensirovannye sredy i mezhfaznye granitsy = Condensed Matter and Interphases, 2007, vol. 9, no. 3, pp. 216–227 (in Russian).
8. Naem A. A. Platinum silicide formation using rapid thermal processing. Journal of Applied Physics, 1988, vol. 64, no. 8, pp. 4161–4167. https://doi.org/10.1063/1.341329
Review
Views: 728
Email this article 